Silver coated copper conductive paint MGT-SCP-9310A is a green alcohol-soluble conductive paint with imported waterborne resins. After sprayed inside housing of electronic products,conductive silver coated copper power forms dense conductive layer film after drying conductive paint film. The dense conductive layer film has functions of good shielding electromagnetic radiation, anti-electromagnetic interference andanti-static. It also has good conductive performance in application ofcomposite materials. This conductive paint is favored by customers because of diluted with alcohol on the plastic housing for corrosion, good adhesion can be hundreds of cells tested, easy to wipe the paint fly, protect fragile shell parts and screw column are not affected by an organic solvent erosion and soon. MGT-SCP-9310A is widely applied in inside housing of various electronic products like GPS, DVD, DVB, medial equipments, etc.
Basic Parameters
ProductName | Silver Coated Copper Conductive Paint |
Model | MGT-SCP-9310A |
Packing specs | 5Kg/pot; 10Kg/pot; 20Kg/pot |
Color | Copper red |
Viscosity | Thixotrophic mixture |
Solid content | 30% |
Theoretical coverage rate | 6-10square /kg ( conductive paint film thickness=20microns ) |
Technical Parameters
Resistivity | less than0.005~0.015 ohm /square per 1.0 mil (25microns) dry film |
Conductive paint application parameters ( Thestate of being coated on a product ) | less than0.08~0.32 ohm / 20 micron thickness / distance 10cm |
Suggestedconductive paint film thickness | 15-25micron ( ASTM D4138-94 ) |
User Guidelines:
1)Paint Mixing: Diluted by ethanol, additive amount of 30%-50%( i.e.1:0.3-0.5 ) by weight ratio of conductive paint.
2)Spraying and tools:
Side pot ora pot of paint spray gun can be used. Caliber is generally 0.3-2.0mm. Smallitems are suggested to use about 0.5mm diameter spray gun, and bulky items use1.5-2.0 diameter spray gun.
Generallydistance of spray gun and spray products should be 100-150mm and not above 200mm. Spray should be uniform and the film thickness should be more than 15microns to achieve good electrical performance.
3) Use materials:
ABS, HIIPS,PS, PC and other plastic parts, and other composite materials or metalmaterials, but it must be not smooth surface. ( Another suitable conductivepaint will be developed if it is used for special materials.)
4) Drying Conditions:
Drytime is 15 minutes; drying time is 30 minutes at 65 degree bake.
Airdry time is more than 4 hours.
5) Test Conditions:
Testshould be done after sprayed conductive paint film has completed cooled anddried.
Notes:
■ Make sure to use side port or apot spray gun to spray conductive paint.
■ Small items are suggested to useK-3 spray gun and large items use W-71 spray gun.
■ Conductive paint should be stirred fully andwell in pot before use, and then it could be diluted. If stirring fully andevenly, metal particles are dispersed evenly to make sprayed conductive paintfilm achieve best conductivity.
■ It is better to stir frequently and stirring frequencyshould be less than 5 minutes to achieve
best performance.
■ Conductive paintshould be used as soon as possible to avoid long term storage after opening.
■ Due to easyprecipitation of metal power, its performance will not be affected after stirring.
■ Protective measures: During using conductive paints, please ensure operating environment is well ventilated and avoid prolonged direct contact or inhalation. Not allowed to pour conductive paint into drains or sewers to pollute environment.
■ Storage:conductive paints are sealed and stored in ventilated and dry indoor environment.
■ Shelf Life: 6months at 25℃ ( intact ).
Disclaimer : The information provided in this Technical Data Sheet (TDS) is compiled in good faith and obtained using procedures performed at Mogreat the best of our knowledge. The information on this TDS has been updated onthe date printed, and latest versions can be obtained upon request. The customer is responsible for conducting tests to determine whether our productsare compatible with the customer's process and specific applications.